Phenolic foam and surfactant useful therein

ABSTRACT

A closed cell phenolic-resin foam material comprising phenolic-resin foam forming reactants, a blowing agent, and a surfactant which is the capped reaction product of an alkoxylated amine and a copolymerizable mixture of dialkyl maleate with N-vinyl-2-pyrrolidone or N-vinyl caprolactam.

This is a divisional of application Ser. No. 935,846, now U.S. Pat. No. 4,204,020, filed Aug. 22, 1978, which is a divisional of application Ser. No. 837,875, filed Sept. 29, 1977, now U.S. Pat. No. 4,140,842.

Phenolic polymers have been known for decades. More recently, there has been increased interest in phenolic polymers which can be formed into cellular materials more commonly referred to as foams. These foams are produced by mixing reactants in the presence of a blowing agent. See for example Thomas et al U.S. Pat. No. 2,744,875 (1956); Nelson Canadian Pat. No. 674,181 (1963); Dijkstra Canadian Pat. No. 684,388 (1964); Wissenfels et al Canadian Pat. No. 866,876 (1971); United Kingdom Specification Pat. No. 598,642 (1948); Australian Pat. No. 128,508 (1945); and Modern Plastics Encyclopedia Volume 53, No. 10a, page 479 (1977). However, most known cellular materials produced from phenolic polymers exhibit an unsatisfactory thermal conductivity initially. Other known cellular materials produced from phenolic polymers exhibit an undesirable increase in thermal conductivity with time.

Accordingly, it is an object of the present invention to provide an improved closed cell phenolic-resin foam material substantially free of the disadvantages of prior foams.

Another object is to provide an improved process for producing improved cellular materials employing an improved phenolic polymer, and an improved laminated building panel employing the improved closed cell phenolic-resin foam material.

A still further object is to provide an improved closed cell phenolic-resin foam material which exhibits a high closed cell content without adversely affecting friability, compressive strength and the low flammability characteristics of the material.

Yet another object is to produce a closed cell phenolic-resin foam material with high thermal resistance and high insulation properties and a substantially slow increase in thermal conductivity with time.

A further object is to produce a closed cell phenolic-resin foam material which can be used as building panels which are highly insulating, thermally resistant, low in friability, soundproof and self-supporting.

Additional objects and advantages of the present invention will be apparent to those skilled in the art by reference to the following detailed description and drawings wherein:

FIG. I is Formula I;

FIG. II is Formula II;

FIG. III is Formula III;

FIG. IV is Formula IV;

FIG. V is Formula V;

FIG. VI is Formula VI;

FIG. VII is Formula VII;

FIG. VIII is a cross-sectional view of a laminated building panel having one facing sheet;

FIG. IX is a cross-sectional view of a laminated building panel having two facing sheets;

FIG. X is a graph showing the relationship between k-factor and time for foams of the present invention.

According to the present invention, there is provided a closed-cell cellular composition comprising a phenolic resin, blowing agent and a surfactant having hydroxyl number of less than 50 preferably less than 10 by reaction with a capping agent. The process of capping functional groups is well known and common agents for masking the functionality of the hydroxyl group are agents which produce esters, urethanes, and ethers. Phenolic resin foams are a well known class, phenolaldehyde resin foams being representative and proportions of blowing agent, catalyst and components are well known in the art.

Foams of low friability can be obtained by using a preferred phenolic polymer described in Moss U.S. Pat. No. 3,876,620. The preferred phenolic polymer is an alkylol group containing phenolic polymer of Formula I shown in FIG. I of the drawings wherein R¹ is ##STR1## hydrogen, or a radical of Formula II.

The R² 's are independently selected from the group consisting of lower alkyl, phenyl, benzyl, halo, nitro, and hydrogen. The R³ 's are independently selected from the group consisting of ##STR2## hydrogen, or a radical of Formula II, shown in FIG. II.

The R⁴ 's are independently selected from the group consisting of lower alkyl, hydrogen, phenyl, benzyl, or furyl. By furyl is meant the radical introduced by the use of furfural. In Formula I, x is an integer from 2 to 10 inclusive and is preferably an integer from 2 to 6 inclusive. When x is less than 2, a foam produced from such a phenolic polymer tends to have too high a friability. On the other hand, as x exceeds 10, the viscosity of the polymer increases to the point where it is difficult to produce the foam. The phenolic polymers of the present invention generally have a molecular weight between 200 and 2,000 and preferably have a molecular weight between 300 and 1,500. At lower molecular weights, the resultant foams tend to have too high a friability, whereas at high molecular weights the viscosity of the phenolic polymer, even when a solvent is present, tends to be too high to permit processing.

A preferred subclass of phenolic polymers are those of Formula III, shown in FIG. III.

In Formula III, R¹ is HOCH₂ --, hydrogen, or a radical of Formula IV.

The R³ 's are independently selected from the group consisting of HOCH₂ --, hydrogen, or a radical of Formula IV, shown in FIG. IV.

In a preferred embodiment of the present invention, at least one of the R³ 's is methylol, i.e., HOCH₂ --. This is to ensure that there will be cross-linking sites on the phenolic polymer. Of course, such methylol groups or, when the aldehyde is other than formaldehyde, alkylol groups, are automatically introduced into the polymer as is well-known in the art by the process described below.

In the broadest aspects of the present invention, the phenolic polymer can contain widely varying ratios of the radicals of Formula II or IV to ortho-cresol units. However, this ratio is generally from 1:3 to 10:1 and is preferably from 1:1.5 to 5:1. At higher ratios, i.e., a deficiency of ortho-cresol, the cellular material produced from such a phenolic polymer tends to be too friable. In determining the above ratios, one must include the radicals of Formula II or IV present in Formula I or III respectively. The synthesis of phenolic polymers of Formulae I through IV is described and claimed in Moss U.S. Pat. No. 3,876,620. These phenolic compositions useful in the present invention generally comprise the phenolic polymer of Formula I or Formula III, together with a compound of Formula V.

The compound of Formula V can be present in the phenolic composition in widely varying ratios of Compound V to polymeric composition but is generally present in a weight ratio of 1:30 to 1:2 and is preferably present in a weight ratio of 1:20 to 1:5. Examples of suitable compounds of Formula V include among others: m-cresol, m-chlorophenol, m-nitrophenol, 3,5-xylenol, and phenol, i.e., hydroxy benzene. Phenol is the most preferred compound of Formula V because of cost, availability, and reactivity. The phenolic polymers of Formula I and Formula III are produced according to the present invention by combining certain reactants in a two-step process described in Moss, supra.

In the broadest aspects of the present invention, any aldehyde can be employed to produce useful phenolic polymers. Examples of suitable aldehydes include among other: furfural, formaldehyde, benzaldehyde, and acetaldehyde. Formaldehyde is the preferred aldehyde. Formaldehyde can be employed in widely varying forms such as the 37% aqueous solution widely known as formalin. However, it is generally necessary to remove from the polymeric material the water introduced with the formalin. Formaldehyde is preferably employed in the form of paraformaldehyde which contains much less water.

The cellular material of the present invention is formed by simply reacting the alkylol group containing phenolic polymer of Formula I or Formula III and the compound of Formula V under conditions such that a cellular product will result. As is well known in the phenolic foam art, the reaction can be conducted in the presence of a foaming catalyst, a blowing agent, and a surfactant. The reaction can be performed between temperatures of 10°-50° C., preferably 15°-25° C., and conveniently at atmospheric pressure. The cellular materials of the present invention generally have a thermal conductivity, k-factor value, of from 0.1 to 0.3 and preferably from 0.1 to 0.2 Btu/hr-°F.-sq. ft per inch as measured at 24° C. The k-factor value is measured on a Model 88 machine supplied by the ANACON Company. The friability of the cellular material is 20% or less. Friability is the propensity of the foam to break expressed in percent weight loss. This is determined by the ASTM C-421 friability test conducted for 10 minutes.

In the broadest aspects of the present invention, any catalyst which will enhance the cross-linking and foaming reaction can be employed in the present invention. However, the preferred foaming catalysts are aromatic sulfonic acids, examples of which include, among others, benzene sulfonic acid, toluene sulfonic acid, xylene sulfonic acid, and phenol sulfonic acid. Phosphoric acid can also be employed either alone or in admixture with the sulfonic acids. The preferred sulfonic acid is a mixture of equal parts by weight of toluene sulfonic acid and xylene sulfonic acid as described in Mausner et al U.S. Pat. No. 3,458,449. Another foaming catalyst which has been found to give excellent results is a blend of toluene sulfonic acid, phosphoric acid, and water in a weight ratio of 35-50:50-35:15.

The catalyst is generally present in the minimum amount that will give the desired cream time of 10 to 50 seconds and firm time of 40 to 500 seconds to the reacting mixture. The catalyst, however, generally comprises from 0.5 to 20, and preferably comprises from 1.0 to 15, weight percent based on the weight of the cellular material. Any blowing agent characteristically employed in similar prior art products such as is described in Moss et al, U.S. Pat. No. 3,968,300, can be employed in the composition of the present invention. In general, these blowing agents are liquids having an atmospheric pressure boiling point between minus 50° and 100° C. and preferably between zero and 50° C. The preferred liquids are hydrocarbons or halohydrocarbons. Examples of suitable blowing agents include, among others, chlorinated and fluorinated hydrocarbons such as trichlorofluoromethane, CCl₂ FCClF₂, CCl₂ FCF₃, diethyl ether, isopropyl ether, n-pentane, cyclopentane, and 2-methylbutane. Combinations of trichlorofluoromethane plus 1,1,2-trichloro, 1,2,2-trifluoroethane, are the preferred blowing agents. The blowing agents are employed in an amount sufficient to give the resultant foam the desired bulk density which is generally between 0.5 and 10, and preferably between 1 and 5 pounds per cubic foot. The blowing agent generally comprises from 1 to 30, and preferably comprises from 5 to 20 weight percent of the composition. When the blowing agent has a boiling point at or below ambient, it is maintained under pressure until mixed with the other components. Alternatively, it can be maintained at subambient temperatures until mixed with the other components.

In the broadest aspects of the instant invention, any hydroxyl containing cell stabilizing surfactant with a branched, non-ionic structure conventionally used in producing polymeric foams can successfully be used after capping the hydroxyl groups. By cell stabilizing surfactant is meant one which keeps a foam from collapsing and rupturing. Typical surfactants have hydroxyl numbers in the range of 60 to 100. In other words, any branched conventional surfactant whose hydroxyl number is reduced to a value of less than 50, preferably less than 10, by reaction with a suitable capping agent such as organic acid, acid anhydride, acid chloride, acyloxy chloride and alkyl or aryl isocyanate is a suitable surfactant. Alcohols can be converted to ethers but this generally does not result in a surfactant that behaves as a cell stabilizer. The hydroxyl number is determined by the ASTM-D1638 test.

The preferred surfactant is the capped reaction product of an alkoxylated amine of Formula VI shown as FIG. 6 wherein R⁵ is an alkoxylated chain of formula VII, n is an integer from 2 to 10 inclusive and the ratio p:q is 15:85 to 85:15, which amine has been reacted with a copolymerizable mixture of dialkyl maleate and a member selected from the group consisting of N-vinyl-2-pyrrolidone and N-vinyl caprolactam, the alkyl of the maleate having 1 to 5 carbon atoms. The preferred dialkyl maleate is dibutyl maleate.

The alkoxylation is carried out using a mixture of ethylene oxide and propylene oxide in the ratio of 15:85 to 85:15 and preferably from 20:80 to 60:40. The molecular weight of the alkoxylated amine is from 1500 to 6000 and preferably from 1800 to 2800. If the molecular weight of the alkoxylated amine is less than 1500, the resultant foam collapses. An alkoxylated amine of molecular weight higher than 6000 is too viscous to be practicable.

The preferred molar ratio of dibutyl maleate and N-vinyl-2-pyrrolidone is 1:1, the mixture of dibutyl maleate and N-vinyl-2-pyrrolidone comprising between 5 and 40 weight percent of the reaction mixture, and preferably 20 weight percent of the reaction mixture. If less than 5 percent is used, the surfactant is ineffective, if more than 40 percent is used, the foam collapses. N-vinyl-2-pyrrolidone and N-vinyl caprolactam are interchangeable in equivalent quantities, but N-vinyl-2-pyrrolidone is preferred.

The capping reaction is carried out with a capping agent. Suitable capping agents include a lower alkyl monocarboxylic acid having 1 to 10 carbon atoms selected from the group consisting of acetic acid, propionic acid, butyric acid, hexanoic acid, octanoic acid, decanoic acid, isomers of these acids, anhydrides of these acids, acid chloride derivatives of these acids and mixtures thereof. Acetic anhydride is readily obtainable and convenient to use. Similarly aromatic acids, anhydrides and chlorides can be employed. Benzoyl chloride and substituted products of it such as 3,5-dinitrobenzoyl chloride are examples of these. Alkyl and aromatic isocyanates can also be employed. Other factors such as solubility in the surfactant and the solubility of the capped surfactant with a particular phenolic-resin are considerations of which a practitioner in the art is cognizant in selecting the system which will yield the desired closed cell stabilized foam. Examples of suitable capping agents are acetic acid, acetic anhydride, acetyl chloride and 3,5-dinitrobenzoyl chloride, reacted so that the surfactant has a hydroxyl value of less than 50, and preferably less than 10. The preferred capping agent is acetic anhydride.

The preferred surfactants useful in the present invention produce a uniform fine-celled foam. Uniformity of cells is determined by visual and microscopic examination. The surfactants must produce a fine celled foam. This property's tested by mixing 2 to 5% of the surfactant with the phenolic composition and producing a foam as described herein. It is interesting to note that a low surface tension of the surfactant in the phenolic-resin is not a prerequisite to obtaining a good foam.

The average cell size diameter must be less than 0.2 mm and is preferably less than 0.1 mm (ASTM D-2842). Fine celled foams can by the means set forth in the invention be rendered closed cells. The blowing agent is then trapped in the cells. One means of expressing the containment in the cells of the blowing agent is by use of the k-factor drift value. Unfaced cellular materials containing fluorocarbon gas have initial k-factors in the vicinity of 0.1-2.0 at 24° C. This low value increases over a period of months or sometimes days. The change is expressed as the k-factor drift. The k-factor is measured at a mean temperature of 24° C. The value is redetermined at various time intervals up to about 1000 days. A material exhibiting fast k-drift will attain a k-factor (Btu/hr-°F.-ft² per inch thickness) of at least 0.2 within 25 days. A slow k-drift material may require between 200 days and over two years to attain a 0.2 value. Any material which possesses a k-value under 0.2 will provide high thermal resistance. Obviously, the longer this value or a lower value is maintained, the better the efficiency of the insulation.

Ball, Hurd and Walker have published a comprehensive discussion of k-factor changes as a function of time. ("The Thermal Conductivity of Rigid Urethane Foams", J. Cellular Plastics, March/April, 1970, pp 66-78.) F. Norton ("Thermal Conductivity and Life of Polymer Foams", J. Cellular Plastics, January, 1967, pp 23-37) has shown that diffusion of fluorocarbon gases out of unfaced foam and infusion of air into the foam causes an increase in k-factor. A slow k-drift foam is defined as one that attains a k-factor at 24° C. of 0.15-0.17 after 200-400 days and then remains below 0.2 k-factor for 5-10 years. Eventually all fluorocarbon diffuses from the foam to leave a closed cell material which contains only air in the cells.

The k-factor for the closed cell foam containing only air falls in the range of 0.22-0.26 Btu/hr-°F.-ft² per inch thickness at 24° C. for the 2-3 lbs/ft³ density range. Therefore, if a foam exhibits greater than 0.2 k-factor after a short period of time (less than 25 days), then substantially all fluorocarbon has diffused from the foam and has been replaced by air. On the other hand, if k-factor remains below 0.2 for at least 100 days then a substantial amount of fluorocarbon gas remains in the closed cells of the foam in spite of infusion of air.

It has been found that capping the surfactant that yields a fine celled foam increases the closed cell content and the initial k-factor is lowered.

Moreover, capping and grafting the surfactant yield a fine celled foam with high closed cell content, a low initial k-factor and a low k-drift value.

The surfactant is employed in a cell stabilizing amount. Generally the surfactant comprises from 0.05 to 10, and preferably comprises from 0.1 to 6, weight percent of the composition. Too little surfactant fails to stabilize the foam and too much surfactant is not only wasteful, but also for surfactants having relatively high surface tension (about 35 dynes/cm) may lead to larger cell structure by cell coalescence and the foam may collapse. Branched, non-ionic, capped, grafted surfactants are preferred.

As used herein any of the allyl, aryl, aralkyl, and/or alkaryl groups can be substituted with one or more groups that do not materially affect the physical or chemical properties of the surfactant compound. Examples of substituents include, among others, --F, --Cl, --Br, --CH₃, and --NO₂.

Referring now to the drawings, and in particular to FIG. VIII, there is shown a laminated building panel 10 of the present invention. The building panel 10 comprises a single facing sheet 11 having thereon a cellular material 12 of the present invention. FIG. IX shows a building panel 20 having two facing sheets 21 and 22 on either side of a cellular material 23.

Any facing sheet previously employed to produce building panels can be employed in the present invention. Examples of suitable facing sheets include, among others, those of kraft paper, aluminum, and asphalt impregnated felts, as well as laminates of two or more of the above.

The invention is further illustrated by the following examples in which all parts and percentages are by weight unless otherwise indicated. These non-limiting examples are illustrative of certain embodiments designed to teach those skilled in the art how to practice the invention and to represent the best mode contemplated for carrying out the invention.

EXAMPLE 1

This example illustrates the synthesis of a phenolic polymer of Formula I useful in the present invention employing a molar ratio of phenol to o-cresol of 2:1.

    ______________________________________                                                            Amount                                                      Item   Ingredient        grams     moles                                       ______________________________________                                         A      o-cresol          10,580    98                                          B      paraformaldehyde (93.6%)                                                                          4,743    148                                         C      sodium hydroxide (50%)                                                                             295     3.69                                        D      phenol            18,428    196                                         E      paraformaldehyde   7,917    247                                         F      glacial acetic acid                                                                                225     3.75                                        ______________________________________                                    

Items A and B are charged to a reaction vessel. Item C is added over a period of fifteen minutes, the temperature rises to 100° C. due to an exothermic reaction and is maintained at that level for 1 hour. Items D and E are then added and the temperature maintained at 80° C. for four and one-half hours. Item F is then added and the contents of the reaction are termed Resin B.

Resin B has a viscosity at 25° C. of 29,500 cps, a free phenol content of 8.1%, and a free water content of 9.1%, a free formaldehyde content of 0.6%, and a free o-cresolcontent of less than 0.1%.

EXAMPLE 2

This example illustrates the synthesis of a phenolic polymer of Formula I useful in the present invention employing a molar ratio of phenol to ortho cresol of 4:1.

The following quantities of the following ingredients are combined as indicated.

    ______________________________________                                                              Amount                                                    Item  Ingredient           grams    moles                                      ______________________________________                                         A     o-cresol              6,901   63.9                                       B     paraformaldehyde (93.5% HCHO)                                                                        3,133   97.7                                       C     sodium hydroxide (50% NaOH)                                                                           215    2.69                                       D     phenol               24,025   255.5                                      E     paraformaldehyde     11,350   354.1                                      F     sodium hydroxide (50% NaOH)                                                                           215    2.69                                       G     glacial acetic acid    350    5.8                                        ______________________________________                                    

Items A and B are charged to a reaction vessel. Item C is added over a period of fifteen minutes, the temperature rises due to the exothermic reaction, to 100° C. and is maintained at that level for 1.5 hours. Items D, E, and F are then added and temperature maintained at 80° C. for 5 hours. Item G is then added and the contents of the reaction vessel is termed Resin C.

Resin C has a viscosity at 25° C. of 24,300 cps, a free phenol content of 8.6%, and a free water content of 10.0%, a free formaldehyde content of 2.3%, and a free o-cresol content of less than 0.1%.

EXAMPLE 3

This example illustrates the synthesis of a surfactant precursor.

    ______________________________________                                                              Amount                                                    Item Ingredient            grams   moles                                       ______________________________________                                         A    ethoxylated propoxylated ethylene                                               diamine (Tetronic 704)                                                                              800     (0.31)                                      B    N-vinyl-2-pyrrolidone 64      0.577                                       C    dibutyl maleate       136     0.596                                       D    azo-bis-isobutyronitrile                                                                             4.0     0.02439                                     E    t-butylperbenzoate    2.0     0.01031                                     ______________________________________                                    

Item A is placed in a reaction vessel at 90° C. Item B is placed in a dropping funnel. Items C, D, and E are mixed together and placed in a second dropping funnel. The contents of the two dropping funnels are each concurrently added to the reaction vessel over a period of one hour while maintaining the temperature at 90° C. The temperature is raised to 140° C. for an additional hour to produce a surfactant precursor.

Item A has a molecular weight of 2600, has a weight ratio of ethylene oxide to propylene oxide of 40:60, and is available from the BASF Wyandotte Corporation, Wyandotte, Michigan, U.S.A., under the tradename "TETRONIC 704".

EXAMPLE 4

This example illustrates the capping or surfactants useful in the present invention.

    ______________________________________                                                           Amount                                                       Item   Ingredient       grams      moles                                       ______________________________________                                         A      surfactant precursor                                                           from Example 3   400        0.154                                       B      acetic anhydride  30        0.294                                       ______________________________________                                    

Items A and B are mixed together at room temperature and heated to 100° C. for two hours to produce a surfactant useful in the present invention termed Surfactant A.

EXAMPLE 5

This example illustrates the synthesis of foaming catalysts useful in the present invention.

The following quantities of the following ingredients are combined as indicated to produce Catalyst A:

    ______________________________________                                         Ingredients               Quantity                                             Item     Name                grams                                             ______________________________________                                         A        p-toluene sulfonic acid                                                                            333                                               B        xylene sulfonic acids                                                                              333                                               C        water               333                                               ______________________________________                                    

Items A, B, and C are mixed. The resultant composition is termed Catalyst A.

The following quantities of the following ingredients are combined as indicated to produce Catalyst B:

    ______________________________________                                         Ingredients               Quantity                                             Item     Name                grams                                             ______________________________________                                         A        Ultra TX            667                                               B        water               333                                               ______________________________________                                    

Items A and B are mixed. The resultant composition is termed Catalyst B. Ultra TX is a mixture of equal parts by weight of p-toluene sulfonic acid and xylene sulfonic acids available from the Witco Chemical Company.

EXAMPLE 6

This example illustrates the synthesis of a foam based on 2:1 phenol:o-cresol resoles of the present invention.

    ______________________________________                                         Item     Ingredient          grams                                             ______________________________________                                         A        Resin B             300                                               B        CFCl.sub.3          22.5                                              C        CCl.sub.2 FCF.sub.2 Cl                                                                             22.5                                              D        Surfactant A of Example 4                                                                          15                                                E        Catalyst B          40                                                ______________________________________                                    

Items A through F are mixed in an open vessel for 15 seconds. The mixture is then poured into a square paper box twelve inches by twelve inches by five inches tall. A foaming reaction ensues. After a period of about 240-300 seconds the material is rigid. The box and contents are placed in an oven at 55° to 75° C. for a period of ten minutes to one hour.

EXAMPLES 7-12

The procedure of Example 6 is repeated using different surfactants. The characteristics of the surfactant and the resultant foam are shown in Table I.

The "TETRONIC" series of alkoxylated amines are available from BASF Wyandotte Corp., Wyandotte, Michigan 48192.

Compressive strength is measured according to ASTM D-1621.

Oxygen Index Value is measured according to ASTM D-2863-74.

A typical resultant foam has the following properties:

Density: 2.4 lbs/ft³

Thermal Conductivity: 0.120 BTU/hr-°F.-ft² per inch

Friability: 12%

Compressive Strength: 30 psi

Oxygen Index Value: 34

FIG. X shows a plot of k-factor versus log time. The k-values are plotted on the y-axis (linear scale) and the time in days is plotted on the x-axis (log scale) as described by Ball, Hurd and Walker, supra.

Fast k-drift materials attain greater than 0.2 k-factors rapidly as shown by curve 1 which are typically represented by Example 8 of Table I. After the k-factor reaches a value of 0.22 the rate of increase slows, tangentially approaching about 0.26.

Slow k-drift materials attain less than 0.2 k-values at 1000 days as shown by curve 2 in FIG. X, which are typically represented by Example 6 of Table I.

It is to be emphasized that these k-values are for 1" thick unfaced (unlaminated) foam boards. Laminated products have superior properties dependent on the permeability of the laminating material and the total surface-exposed edge proportions.

                  TABLE I                                                          ______________________________________                                         PROPERTIES OF PHENOLIC FOAMS MADE                                              WITH 2:1 PHENOL:O-CRESOL BASED RESINS                                          1     2        3        4     5    6      7                                                   Co-            Den- Initial K                                                                             k arift                              Ex-   Alkoxy-  polymer        sity (btu/hr-                                                                              dk                                   ample lated    Level    Ratio (lb/ °F.-ft.sup.2                                                                   dLogt                                (No.) Amine    (Wt.%)   p:q   ft.sup.3)                                                                           per inch)                                                                             (× 10.sup.3)                   ______________________________________                                         6     Tetronic 20       40:60 2.4  0.120  6                                          704                                                                      7     Tetronic 20       20:80 2.3  0.128  5                                          702                                                                      8     Tetronic 20       40:60 2.3  0.144  30                                         504                                                                      9     Tetronic 30       20:80 2.3  0.128  9                                          702                                                                      10    Tetronic 30       40:60 2.7  0.128  9                                          704                                                                      11    Tetronic 10       20:80 2.6  0.13   24                                         702                                                                      12    Tetronic 10       40:60 2.6  0.128  9                                          704                                                                      ______________________________________                                    

EXAMPLE 13

This example illustrates the synthesis of a foam based on 4:1 phenol: o-cresol resole of the present invention.

    ______________________________________                                         Item               Ingredient                                                                               grams                                             ______________________________________                                         A        Resin C             300                                               B        CFCl.sub.3          22.5                                              C        CFCl.sub.2 CF.sub.2 Cl                                                                             22.5                                              D        Surfactant A of Example 4                                                                          15                                                E        Catalyst B          35                                                ______________________________________                                    

Items A through E are mixed in an open vessel for 15-20 seconds. The mixture is then poured into a square paper box twelve inches by twelve inches by five inches tall. A foaming reaction ensues. After a period of 300-400 seconds the material is rigid. The box and contents are placed in an oven at 55° to 75° C. for a period of ten minutes to one hour.

EXAMPLES 14-16

The procedure of Example 6 is repeated using different surfactants. The characteristics of the surfactant and resultant foam are shown in Table II.

A typical resultant foam has the following properties:

Density: 2.2 lbs/ft³

Thermal Conductivity: 0.13 Btu/hr-°F.-ft² per inch

Friability: 32%

Compressive Strength: 25 p

Oxygen Index Value: 40

                                      TABLE II                                     __________________________________________________________________________     PROPERTIES OF PHENOLIC FOAMS MADE                                              WITH 4:1 PHENOL:O-CRESOL BASED RESINS                                                                           k drift                                                   Copolymer      Initial k                                                                            dK                                            Example                                                                             Alkoxylated                                                                           Level Ratio                                                                              Density                                                                             (Btu/hr-°F.-                                                                  dLogt                                                                               Catalyst B                               (No.)                                                                               Amine  (Wt.%)                                                                               p:q (lb/ft.sup.3)                                                                       ft.sup.2 per inch)                                                                   (× 10.sup.3)                                                                  phr                                      __________________________________________________________________________     14   Tetronic 704                                                                          20    40:60                                                                              2.2  0.13  9    11.7                                     15   Tetronic 704                                                                          20    40:60                                                                              2.3  0.13  5    13.3                                     16   Tetronic 702                                                                          20    20:80                                                                              2.3  0.12  5    11.7                                     __________________________________________________________________________

Although the invention has been described in considerable detail with reference to certain preferred embodiments thereof, it will be understood that variations and modifications can be effected within the spirit and scope of the invention as described above and as defined in the appended claims. 

We claim:
 1. A surfactant which is the reaction product of:I. an alkoxylated amine of the formula ##STR3## wherein: (a) R⁵ is an alkoxylated chain of the formula ##STR4## (b) n is an integer from 2 to 10 inclusive, (c) the ratio p:q is 15:85 to 85:15 with II. a copolymerizable mixture of dialkyl maleate and a member selected from the group consisting of N-vinyl-2-pyrrolidone and N-vinyl caprolactam, wherein the molar ratio of dibutyl maleate to said N-vinyl member is 1:1, and III. a capping agent for the terminal hydroxyl groups which eliminates the active hydrogen of said groups.
 2. A surfactant which is the reaction product of:I. an alkoxylated amine of the formula ##STR5## wherein: (a) R⁵ is an alkoxylated chain of the formula ##STR6## (b) n is an integer from 2 to 10 inclusive, (c) the ratio p:q is 20:80 to 60:40,(d) the molecular weight of the alkoxylated amine is 1800 to 2800, II. a copolymerizable mixture of dibutyl maleate and N-vinyl-2-pyrrolidone wherein the copolymerizable mixture comprises 20 weight percent based on the weight of the reaction product, and the molar ratio of dibutyl maleate to N-vinyl-2-pyrrolidone is 1:1, and III. acetic anhydride, wherein the surfactant has a hydroxyl value less than
 10. 3. The surfactant of claim 1 wherein the alkyl of the maleate has 1 to 5 carbon atoms.
 4. The surfactant of claim 1 wherein the molecular weight of the alkoxylated amine is from 1800 to
 2800. 5. The surfactant of claim 1 wherein the ratio p:q is 20:80 to 60:40.
 6. The surfactant of claim 1 wherein the ratio p:q is 20:80 to 60:40, and the alkyl of the maleate has 1 to 5 carbon atoms.
 7. The surfactant of claim 6 wherein the molecular weight of the alkoxylated amine is from 1800 to
 2800. 8. The surfactant of claims 3, 4, 5, 6 or 7 wherein the surfactant has a hydroxyl value of less than
 50. 9. The surfactant of claim 8 wherein the surfactant has a hydroxyl value of less than
 10. 10. The surfactant of claim 1 wherein the component II copolymerizable mixture comprises dibutyl maleate and N-vinyl-2-pyrrolidone.
 11. The surfactant of claim 10 wherein the ratio of p:q is 20:80 to 60:40.
 12. The surfactant of claim 11 wherein the molecular weight of the alkoxylated amine is from 1800 to
 2800. 13. The surfactant of claims 10, 11, or 12 wherein the component II copolymerizable mixture comprises between 5 and 40 weight percent of the reaction mixture, and the molar ratio of dibutyl maleate and N-vinyl-2-pyrrolidone is 1:1.
 14. The surfactant of claim 13 wherein the component II copolymerizable mixture comprises 20 weight percent of the reaction mixture.
 15. The surfactant of claim 13 wherein the surfactant has a hydroxyl value of less than
 50. 16. The surfactant of claim 15 wherein the component II copolymerizable mixture comprises 20 weight percent of the reaction mixture.
 17. The surfactant of claim 13 wherein the surfactant has a hydroxyl value of less than
 10. 18. The surfactant of claim 17 wherein the component II copolymerizable mixture comprises 20 weight percent of the reaction mixture. 